Solvay Specialty Polymers Xydar® G-930 Liquid Crystal Polymer (LCP), 30% Glass Fiber
Material Notes: Xydar® G-930 Liquid Crystal Polymer (LCP) is a glass reinforced injection molding grade developed specifically for electrical/electronic applications utilizing surface mount technology.
The moldability of this resin is exceptional. Xydar® G-930 can fill very thin walls over long flow lengths with little or no flash, even at mold temperatures below 200°F (93°C). In addition, it has low warpage in molded products and exceptional weld line strength.
Features:: Flame Retardant; Good Chemical Resistance; Good Moldability; Good Weather Resistance; High Stiffness; High Strength; Low Warpage; Radiation (Gamma) Resistant
Uses: Automotive Applications; Automotive Electronics; Bobbins; Electrical Parts; Electrical/Electronic Applications; Industrial Applications; Industrial Parts
Automotive Specifications ASTM D5138 LCP0110 G30 B00000; DELPHI M-5282 M5282 Color: BK Black
Information provided by Solvay Specialty Polymers.
重要參數：
| Physical Properties | Metric | English | Comments |
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Filler Content | 0.3 | 0.3 | Glass Fiber |
| Water Absorption | <= 0.100 % | <= 0.100 % | ISO 62 |
| @Time 86400 sec | @Time 24.0 hour | ||
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 135 MPa | 19600 psi | ASTM D638 |
| Elongation at Break | 0.016 | 0.016 | ASTM D638 |
| Tensile Modulus | 15.9 GPa | 2310 ksi | ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 13.4 GPa | 1940 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.30 J/cm | 8.06 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.9 | 3.9 | ASTM D150 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ||
| 4.2 | 4.2 | ASTM D150 | |
| @Frequency 60.0 Hz | @Frequency 60.0 Hz | ||
| Dielectric Strength | 39.0 kV/mm | 991 kV/in | ASTM D149 |
| @Thickness 1.57 mm | @Thickness 0.0618 in | ||
| Arc Resistance | >= 300 sec | >= 300 sec | ASTM D495 |
| Comparative Tracking Index | 185 V | 185 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 3.60 - 7.20 µm/m-°C | 2.00 - 4.00 µin/in-°F | |
| CTE, linear, Transverse to Flow | 40.0 - 79.0 µm/m-°C | 22.2 - 43.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 271 °C | 520 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 220 °C | 428 °F | |
| @Thickness 0.750 mm | @Thickness 0.0295 in | ||
| UL RTI, Mechanical with Impact | 200 °C | 392 °F | |
| @Thickness 0.750 mm | @Thickness 0.0295 in | ||
| UL RTI, Mechanical without Impact | 220 °C | 428 °F | |
| @Thickness 0.750 mm | @Thickness 0.0295 in | ||
| Flammability, UL94 | V-0 | V-0 | |
| @Thickness 0.400 mm | @Thickness 0.0157 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 321 - 360 °C | 610 - 680 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| @Time 21600 - 28800 sec | @Time 6.00 - 8.00 hour | ||
| Descriptive Properties | |||
| Availability | Asia Pacific | ||
| Europe | |||
| North America | |||
| Clamp Tonnage | 2.8 to 5.5 kN/cm² | ||
| Color | Black; Natural | ||
| Form | Pellets | ||
| Processing Technique | Injection Molding | ||
| RoHS Compliance | RoHS Compliant | ||
| Screw Compression Ratio | 2.5:1.0 to 3.0:1.0 | ||
| Screw L/D Ratio | 20.0:1.0 to 24.0:1.0 |
生產廠商：美國蘇威先進聚合物公司 [查看報價]
產品特性：高溫電氣 / 電子裝配：能承受 SMT 裝配工序操作，包括無鉛回流焊接。 卓越的暖老化性能，在高溫下保持固有特性。 卓越的流動性 - 薄壁，復雜的形狀。 尺寸穩定性極佳，模塑收縮率低，熱膨脹系數極小，可與金屬相媲美。 在成型時，分子鏈朝著流動的方向排列，產生一種好似其分子自身將其增強的自增強效果可獲得極高的強度和彈性模量。 優異的耐化學腐蝕性。 模塑速度：周期循環極快。 卓越的抗蠕變性。 阻燃性。 在寬廣的溫度范圍內具有卓越的介電性